| 产品特性：注塑级 | 是否进口：否 | 产地：美国 |
| 厂家(产地)：美国陶氏 | 牌号： 9007 | 类型：标准料 |
| 品名：OBC | 加工级别：注塑级 | 特性级别：标准级 |
| 用途级别：通用级 | 品牌：美国陶氏 |
INFUSE? 9007
Olefin Block Copolymer
The Dow Chemical Company
产品说明：
INFUSE? 9007 Olefin Block Copolymer is a lower density higher performance olefin block copolymer that can be widely used in TPE applications where higher service temperature requirements are needed. INFUSE 9007 also provides high filler loading capability and gives good elastic recovery.
Main Characteristics:
High upper service temperature performance
Highly flexible with good elastic recovery
General purpose elastomer
Excellent for compounds and blends
Talc dusted
Complies with
EU, No 10/2011
U.S. FDA FCN 424
Consult the regulations for complete details.
| 基本信息 | |
|---|---|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.866 | g/cm? | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A, 模压成型) | 64 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 - *** 正割 (模压成型) | 1.78 | MPa | ASTM D638 |
| 抗张强度 (断裂, 模压成型) | 4.07 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 400 | % | ASTM D638 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (断裂) | 9.70 | MPa | ASTM D412 |
| 伸长率 (断裂) | 1300 | % | ASTM D412 |
| 撕裂强度 | 29.0 | kN/m | ASTM D624 |
| 压缩***变形 | ASTM D395 | ||
| 21°C | 18 | % | ASTM D395 |
| 70°C | 57 | % | ASTM D395 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 溶融温度（DSC） | 119 | °C | 内部方法 |
| TMA 1(1.00 mm) | 88 | °C | 内部方法 |